Download or read book ETUDE DE L OXYDATION A HAUTE TEMPERATURE DES REVETEMENTS NICRAIY ELABORES PAR TRAITEMENT LASER A PARTIR DE POUDRES PRE ALLIEES ANALYSE DES PARAMETRES STRUCTURAUX PHYSICO CHIMIQUES ET MECANIQUES written by FLAVIO SANDRO.. LAYS CASSINO and published by . This book was released on 1998 with total page 175 pages. Available in PDF, EPUB and Kindle. Book excerpt: L'OBJET DE CE TRAVAIL EST D'ETUDIER LE COMPORTEMENT, SOUS OXYDATION ISOTHERME, D'ALLIAGES NICRAIY DANS LE DOMAINE DE TEMPERATURE ALLANT DE 800\C A 1200\C. CES ALLIAGES ONT ETE ELABORES, SOUS FORME DE REVETEMENTS DE SURFACE, PAR PROJECTION DE POUDRES PRE-ALLIEES AVEC FUSION PAR FAISCEAU LASER. DEUX REVETEMENTS, NI 6 4CR 2 5AL 1 0Y 0 . 2 ET NI 5 8CR 2 4AL 1 7Y 0 . 5, ONT ETE ANALYSES. L'ETUDE A PORTE SUR LES ASPECTS CINETIQUES, MORPHOLOGIQUES ET MECANIQUES DU PROCESSUS D'OXYDATION A HAUTE TEMPERATURE DES REVETEMENTS LASER ET, EN PARTICULIER, SUR LA RELATION ENTRE LA MICROSTRUCTURE TYPIQUE DE TELS ALLIAGES AVEC LA FORMATION ET LA TENUE MECANIQUE DE LA COUCHE D'OXYDE. LES RESULTATS OBTENUS POUR LES DEUX NUANCES MONTRENT QUE LE COMPORTEMENT GLOBAL, SOUS OXYDATION, EST ANALOGUE A CEUX, DEJA DECRIT DANS LA LITTERATURE, D'ALLIAGES DE COMPOSITIONS CHIMIQUES COMPARABLES A CELLES DES DEPOTS. LA COUCHE D'OXYDE EST FORMEE, ESSENTIELLEMENT, D'AL 2O 3, SOIT SOUS FORME STABLE (AL 2O 3), SOIT SOUS FORMES METASTABLES (AL 2O 3, AL 2O 3, ETC.). CEPENDANT, EN FONCTION DES CARACTERISTIQUES MICROSTRUCTURALES ET MICROCHIMIQUES DE CE TYPE DE REVETEMENT, DES DIFFERENCES IMPORTANTES ONT ETE MISES EN EVIDENCE. EN PARTICULIER, IL A ETE MONTRE QUE LE PROCESSUS DE DEPOT INDUIT UNE DISTRIBUTION EN YTTRIUM CAPABLE D'AFFECTER LE DEVELOPPEMENT DE LA COUCHE D'ALUMINE DES LE DEBUT DU PROCESSUS D'OXYDATION. DES REGIONS DE DECOLLEMENT D'OXYDE ONT ETE MISES EN RELATION AVEC LA DISTRIBUTION EN YTTRIUM. EN DESSUS DE 1000\C CES DECOLLEMENTS D'OXYDE N'ONT PAS ETE OBSERVES ; TEMOIGNANT UN MECANISME DE CICATRISATION. L'EXISTENCE D'UNE VAPORISATION A HAUTE TEMPERATURE A ETE IDENTIFIEE, QUI PEUT JOUER SUR LA RELAXATION DES CONTRAINTES. LES CONTRAINTES RESIDUELLES APRES

Download or read book ELABORATION ET ETUDE DE LA TENUE A L OXYDATION A HAUTE TEMPERATURE D ALLIAGES DE SURFACE OBTENUS PAR IRRADIATION LASER SUR DEUX ACIERS FERRITIQUES PEU ALLIES written by ENORI.. GEMELLI and published by . This book was released on 1995 with total page 159 pages. Available in PDF, EPUB and Kindle. Book excerpt: L'OBJECTIF DU TRAVAIL PRESENTE ICI EST D'AUGMENTER, PAR UN TRAITEMENT DE SURFACE, LA TENUE A L'OXYDATION A TEMPERATURE ELEVEE ET LA DURETE D'ACIERS FERRITIQUES FAIBLEMENT ALLIES. NOUS PRESENTONS LES RESULTATS OBTENUS AVEC LES ACIERS 35NCD16 ET Z38CDV5 PAR IRRADIATION LASER ASSURANT L'INCORPORATION SUPERFICIELLE ET LA DISSOLUTION DE PREDEPOTS DE NITRURES (ALN, SI#3N#4) OU DE CARBURES (SIC, CR#3C#2). NOUS PRECISIONS LES CONDITIONS D'OBTENTION D'ALLIAGES DE SURFACE EXEMPTS DE FISSURES, D'AMAS OU DE POROSITES. LA DURETE DE CES ALLIAGES DEPEND PRINCIPALEMENT DE LA FORMATION DE MARTENSITE ET (OU) DE LA PRECIPITATION DE CARBURES OU DE NITRURES. L'EXCELLENTE TENUE A L'OXYDATION EN CONDITIONS ISOTHERMES JUSQU'A 950C DE QUELQUES ALLIAGES DE SURFACE DANS UNE ATMOSPHERE D'OXYGENE RESULTE ESSENTIELLEMENT DE LA FORMATION D'UNE COUCHE D'OXYDE DE CHROME CR#2O#3. DANS LES ALLIAGES CONTENANT DU SILICIUM ET RELATIVEMENT PEU DE CHROME, LA CROISSANCE DE CETTE COUCHE DE CR#2O#3 N'INTERVIENT QU'APRES CELLE, INITIALE, D'UNE TRES MINCE PELLICULE DE SILICE QUI INHIBE L'OXYDATION DU FER ET REND POSSIBLE LE DEVELOPPEMENT DE LA COUCHE PROTECTRICE DE CR#2O#3. LE BON COMPORTEMENT EN CYCLAGE THERMIQUE DES ALLIAGES DE SURFACE ETUDIEES SUR L'ACIER Z38CDV5 RESULTERAIT DE LA CROISSANCE DE CR#2O#3 PAR DIFFUSION ANIONIQUE. LA PETITE TAILLE DE GRAINS DE CET OXYDE PERMETTRAIT UNE BONNE RELAXATION DE CONTRAINTES THERMIQUES PAR DEFORMATION PLASTIQUE. NOUS AVONS DONC MONTRE QUE LE TRAITEMENT LASER AVEC AJOUT PEUT CONSTITUER UN PROCEDE EFFICACE POUR CONFERER AUX ACIERS PEU ALLIES UN COMPORTEMENT EN OXYDATION A HAUTE TEMPERATURE TOUT A FAIT COMPARABLE A CELUI DES ACIERS INOXYDABLES AVEC L'AVANTAGE D'UNE DURETE PLUS ELEVEE

Download or read book Etude de l Evolution Physico Chimique du Substrat lors de l Oxydation Haute Temp rature des Alliages Mod le Ni Cr Faible Teneur en Chrome et de l Alliage Mod le Ni 16Cr 9Fe written by André Nicolas and published by . This book was released on 2012 with total page 0 pages. Available in PDF, EPUB and Kindle. Book excerpt: Le travail réalisé au cours de cette thèse concerne l'analyse des conséquences de l'oxydation à 950°C des alliages base Ni sur la composition de l'alliage à proximité de l'interface alliage/oxyde. Deux catégories d'alliages ont été analysées : alliages à faible teneur en chrome conduisant à l'oxydation interne et l'alliage chromino-formeur Ni-16Cr-9Fe.Une description complète des mécanismes de l'oxydation interne du chrome est obtenue à partir du développement du modèle analytique de Wagner d'oxydation interne et du développement du modèle numérique de Feulvarch. Ces modèles décrivent l'évolution de l'oxydation interne jusqu'à la transition oxydation interne / oxydation externe à 11 %poids de chrome environ.L'analyse par la spectroscopie d'électrons Auger de l'alliage modèle Ni-16Cr-9Fe à 950°C oxydé pendant 10 heures a permis d'explorer la zone à proximité immédiate de l'interface alliage/oxyde et de déterminer la concentration en chrome à l'interface à 0,5%poids (i.e. dans 20 premiers nanomètres), ce qui est en accord avec le modèle analytique de Wagner d'oxydation en couche compacte. La description des profils de déchromisation et des profils de cavités pour plusieurs temps d'exposition allant de 100h à 5000h a permis de mettre en évidence une corrélation forte entre ces deux phénomènes (même constante parabolique). Pour ces durées d'oxydation les profils de déchromisation présentent un point d'inflexion ce qui se traduit par l'augmentation de la teneur en chrome à l'interface. Les résultats sont interprétés dans le cadre d'un nouveau modèle analytique avec l'hypothèse d'injection des lacunes produites par l'effet Kirkendall au point d'inflexion.