Download or read book INFLUENCE DE LA PHASE INTERGRANULAIRE SUR L OXYDATION DE CERAMIQUES A BASE DE NITRURE DE SILICIUM SI 3N 4 PUR OU DENSIFIE AVEC AJOUTS DE MGO Y 2O 3 ET AL 2O 3 written by VALERIE.. GUERIN and published by . This book was released on 2000 with total page 254 pages. Available in PDF, EPUB and Kindle. Book excerpt: SI LES CERAMIQUES PURES ( OU ) FORMENT, EN ATMOSPHERE OXYDANTE, UN FILM PROTECTEUR DE CRISTOBALITE, LES MATERIAUX FRITTES AVEC AJOUTS PRESENTENT UNE RESISTANCE A L'OXYDATION MOINDRE A HAUTE TEMPERATURE. SELON LA NATURE DES ADDITIFS DE FRITTAGE, DES MICROSTRUCTURES OXYDEES TRES DIFFERENTES ONT MIS EN EVIDENCE LE ROLE ESSENTIEL DE LA PHASE INTERGRANULAIRE ET ONT SERVIS DE BASE A DES MODELES PRECIS D'OXYDATION DE CERAMIQUES DENSIFIEES A BASE DE SI 3N 4. LES FACTEURS GOUVERNANT LA CORROSION DU NITRURE DE SILICIUM ONT ETE DETAILLES AUTOUR DE L'INFLUENCE DE LA PHASE INTERGRANULAIRE ; SELON : $ SES PROPRIETES DIFFERENTES (TRANSPORT DIFFUSIF, DISSIPATION DES CONTRAINTES D'OXYDATION) ; $ LA PROPORTION ET LA DISTRIBUTION DE LA PHASE VITREUSE SILICATEE EN FONCTION DE LA DEVITRIFICATION ET DE LA DEMIXTION EN PHASE AMORPHE. L'INFLUENCE NEFASTE DE L'ALUMINE A ETE CONFIRMEE A PARTIR DES CINETIQUES PARABOLIQUES D'OXYDATION, PUIS JUSTIFIEE PAR LA DISTRIBUTION UNIFORME ET ETENDUE DE SILICATES FAIBLEMENT VISQUEUX, QUI ABAISSENT LA TEMPERATURE EUTECTIQUE DE LA COUCHE D'OXYDE. EN REVANCHE, LES OXYDES DE TERRES RARES (Y 2O 3), OU LA MAGNESIE FORMENT DE COUCHES D'OXYDE MAJORITAIREMENT CRISTALLISEES, QUI LIMITENT LES CHEMINS RAPIDES DE DIFFUSION (PHASES AMORPHES). LES MODELES D'OXYDATION PROPOSES TIENNENT COMPTE DE LA COMPLEXITE DES SYSTEMES POLYCRISTALLINS : REACTION PASSIVE D'OXYDATION, DIFFUSIONS ANIONIQUE ET CATIONIQUE, OXYDATION INTERNE, LA REDUCTION DES SECTIONS EFFICACES DE DIFFUSION PAR DEMIXTION OU DEVITRIFICATION EN PHASE AMORPHE LA TRANSITION ALLOTROPIQUE A ETE SUIVIE POUR LA PREMIERE FOIS IN SITU (MET) ET LES PREMIERS STADES DE LA TRANSFORMATION ONT ETE CARACTERISES A L'ECHELLE MICROSCOPIQUE. L'INFLUENCE DE LA MICROSTRUCTURE INITIALE SUR LA RESISTANCE A L'OXYDATION DES CERAMIQUES PURES (POROSITE, TAILLE DE GRAINS, LARGEUR DES JOINTS DE GRAINS, PHASE , ), ET LE ROLE DE L'OXYNITRURE ONT FINALEMENT ETE DETAILLES.

Download or read book COMPORTEMENT A L OXYDATION DE CERAMIQUES A BASE DE NITRURE DE SILICIUM EN ATMOSPHERE COMPLEXE AIR SO 2 written by JEAN-BERNARD.. VEYRET and published by . This book was released on 1989 with total page pages. Available in PDF, EPUB and Kindle. Book excerpt: L'ETUDE DE L'INFLUENCE DE LA MICROSTRUCTURE DE NITRURES DE SILICIUM FRITTES SUR LES LOIS DE COMPORTEMENT DANS L'AIR CHARGE DE GAZ SULFUREUX A HAUTE TEMPERATURE A PERMIS DE PRECISER DANS UN PREMIER TEMPS LEUR RESISTANCE A L'OXYDATION EN ATMOSPHERE EXEMPTE DE SOUFRE. ON PEUT DISTINGUER DEUX GRANDS TYPES DE MATERIAUX, CEUX COMPORTANT DES PHASES VITREUSES RESIDUELLES RESULTANT DE L'EMPLOI D'AJOUTS ALCALINO-TERREUX ET CEUX BEAUCOUP PLUS RARES, PRESENTANT DES PHASES SECONDAIRES CRISTALLINES PRECIPITANT AISEMENT; C'EST LE CAS DE L'YTTRIUM UTILISE COMME AJOUT DE FRITTAGE. UNE ATMOSPHERE COMPLEXE AIR-SO#2 NE MODIFIE PAS LES MECANISMES D'OXYDATION, NI LE COMPORTEMENT MECANIQUE A HAUTE TEMPERATURE. L'INFLUENCE DU SOUFRE EN ATMOSPHERE OXYDANTE N'EST DONC PAS A CRAINDRE; ELLE PEUT MEME ETRE BENEFIQUE DANS CERTAINS CAS OU INTERVIENT L'YTTRIUM SI LES SULFATES FORMES A PARTIR D'IMPURETES MINEURES, TELLES LE CALCIUM OU LE SODIUM PERMETTENT UNE MEILLEURE STABILITE DU REVETEMENT PROTECTEUR FORME AU COURS DE L'OXYDATION

Download or read book Interaction de c ramiques non oxydes Si3N4 SiC AlN avec l aluminium liquide written by Luc Mouradoff and published by . This book was released on 1994 with total page 149 pages. Available in PDF, EPUB and Kindle. Book excerpt: LA REACTIVITE DE CERAMIQUES NON-OXYDES (SI#3N#4, SIC ET ALN), EN CONTACT AVEC L'ALUMINIUM LIQUIDE, A ETE ETUDIEE AFIN DE CHOISIR UN MATERIAU UTILISABLE POUR LA REALISATION DE GAINES PROTECTRICES DE THERMOPLONGEURS, EN VUE D'UNE APPLICATION INDUSTRIELLE. LA STABILITE INTRINSEQUE DE CES TROIS CERAMIQUES EST TESTEE EN UTILISANT DES MATERIAUX PURS, ELABORES PAR DEPOT CHIMIQUE EN PHASE VAPEUR (SI#3N#4, SIC), OU PAR COMPRESSION ISOSTATIQUE A CHAUD (ALN). LES ESSAIS DE MOUILLABILITE PAR LA METHODE DE LA GOUTTE POSEE, DE CORROSION PAR LA METHODE DES DOIGTS PLONGEANTS ET D'OXYDATION SONT COUPLES A DES OBSERVATIONS MORPHOLOGIQUES, A LA CARACTERISATION PHYSICO-CHIMIQUE DES INTERFACES AINSI QU'A DES CALCULS THERMODYNAMIQUES. LA COMPARAISON DES RESULTATS AVEC CEUX OBTENUS A PARTIR DE PRODUITS INDUSTRIELS (SIC RECRISTALLISE ET SI#3N#4 FRITTE REACTION) ET DES CONSIDERATIONS ECONOMIQUES ONT PERMIS DE DETERMINER LA CERAMIQUE LA PLUS APTE A REMPLIR LE ROLE DE GAINE PROTECTRICE DE THERMOPLONGEUR: LE NITRURE DE SILICIUM. EN VUE DE L'INDUSTRIALISATION DU PRODUIT, CE NITRURE A ENSUITE ETE FRITTE A L'AIDE D'AJOUTS SOIGNEUSEMENT CHOISIS (Y#2O#3 ET AL#2O#3) DE FACON A DENSIFIER LA CERAMIQUE SANS ALTERER SES CARACTERISTIQUES (TENUE A L'OXYDATION, AUX CHOCS THERMIQUES ET A LA CORROSION PAR L'ALUMINIUM LIQUIDE). LE NITRURE DE SILICIUM AINSI OBTENU EST FINALEMENT CARACTERISE (PROPRIETES MECANIQUES, RESISTANCE A LA CORROSION) AFIN D'ETABLIR D'ETROITES CORRELATIONS ENTRE CONDITIONS D'ELABORATION, MICROSTRUCTURE ET PROPRIETES

Download or read book Comportement m canique et r sistance l oxydation de nitrures de silicium et titane densifi s ou post densifi s par compression isostatique chaud written by Luc Themelin and published by . This book was released on 1989 with total page pages. Available in PDF, EPUB and Kindle. Book excerpt: LA TECHNIQUE DE COMPACTION ISOSTATIQUE A CHAUD A ETE MISE A PROFIT POUR REALISER DES CERAMIQUES DENSES DE TYPE NITRURE. LEUR ELABORATION A NECESSITE LA MISE AU POINT D'UN PROTOCOLE DE FABRICATION DIFFERENT POUR CHAQUE MATERIAU. DANS UN PREMIER TEMPS, UN TRAITEMENT DE POST-DENSIFICATION A ETE EFFECTUE SUR DEUX NUANCES DE NITRURES DE SILICIUM FRITTES NATURELLEMENT EN PRESENCE D'AJOUTS (Y#2O#3, AL#2O#3, ALN ET MG AL#2O#4). NON SEULEMENT LA DENSITE MAIS AUSSI LES PROPRIETES MECANIQUES: RESISTANCE A LA FLEXION, MICRODURETE, TENACITE ONT ETE AMELIOREES. EN REVANCHE, LA TENUE A L'OXYDATION DANS L'AIR DU MATERIAU TRAITE RESTE COMPARABLE A CELLE DU MATERIAU INITIAL. CES RESULTATS ONT ETE PARFAITEMENT EXPLIQUES PAR LES ANALYSES MICROSTRUCTURALES DES PHASES AUX JOINTS DE GRAINS EFFECTUEES EN MICROSCOPIE ELECTRONIQUE A TRANSMISSION. LA DEUXIEME ETUDE A CONCERNE LE FRITTAGE DIRECT EN ENVELOPPE DE SILICE D'UNE POUDRE FINE DE NITRURE DE SILICIUM ADDITIONNEE DE 0,5% D'OXYDE D'YTTRIUM. LE MATERIAU OBTENU EST PARFAITEMENT DENSIFIE. SES PROPRIETES MECANIQUES SONT ANALYSEES ET COMPAREES A CELLES DES MATERIAUX POST-FRITTES PAR C.I.C. SA RESISTANCE A L'OXYDATION EST EXCELLENTE JUSQU'A 1600#OC. L'ETUDE MET BIEN EN EVIDENCE L'INFLUENCE DE LA MICROSTRUCTURE SUR LES LOIS DE COMPORTEMENT DANS L'AIR. LE DERNIER CHAPITRE TRAITE DU FRITTAGE PAR C.I.C. D'UNE POUDRE DE NITRURE DE TITANE DANS UNE ENVELOPPE EN TITANE. L'EVOLUTION DE LA POROSITE EN FONCTION DE LA PRESSION APPLIQUEE ET LA DUREE DE TRAITEMENT. L'OPTIMISATION DES CONDITIONS OPERATOIRES A CONDUIT A L'OBTENTION D'UN MATERIAU PARFAITEMENT DENSE DONT LA RESISTANCE MECANIQUE, LA TENUE AUX CHOCS THERMIQUES ET A L'OXYDATION ONT ETE CARACTERISEES

Download or read book CERAMIQUES DU SYSTEME LN SI O N written by Jean-Jacques Anguile and published by . This book was released on 1987 with total page 66 pages. Available in PDF, EPUB and Kindle. Book excerpt: ON A PREPARE DIVERS MATERIAUX DU SYSTEME LN::(2)O::(3)-SI::(3)N::(4) PAR FRITTAGE OU FUSION HAUTE TEMPERATURE, EN MILIEU CARBONE OU NON CARBONE. A PARTIR D'UNE PROPORTION DONNEE SE FORMENT AU FRITTAGE DES OXYNITRURES QUI LIMITENT LA CARBURATION DES MELANGES A LA FUSION. POUR DES TENEURS EN NITRURE PLUS IMPORTANTES APPARAISSENT SI METALLIQUE ET UNE PHASE MIXTE DE SI ET DE LANTHANIDE NON IDENTIFIEE INSENSIBLE AU CARBONE, A L'AIR ET A L'EAU. LE DEGAGEMENT D'AZOTE LORS DE LA DECOMPOSITION DU NITRURE REND LES MATERIAUX POREUX. UN CREUSET A ETE MIS AU POINT POUR PROTEGER LES ECHANTILLONS DE LA CARBURATION. L'EXISTENCE D'UN GRAND NOMBRE DE NOUVELLES PHASES NON IDENTIFIEES A ETE MISE EN EVIDENCE. DE FAIBLES AJOUTS DE SI::(3)N::(4) PERMETTENT D'ABAISSER LE POINT DE FUSION DES OXYDES DE LANTHANIDES, MAIS PAS LA TEMPERATURE EUTECTIQUE DU BINAIRE LA::(2)O::(3)-AL::(2)O::(3). DE FAIBLES AJOUTS DE LA::(2)O::(3) NE SUFFISENT PAS A ABAISSER LE POINT DE FUSION DES SIALONS