Download or read book ETUDE PAR XPS DE L EFFET ANTAGONISTE DU SOUFRE ET DU CHROME SUR LA PASSIVATION D ALLIAGE SNI CR FE written by JEAN MICHEL.. GRIMAL and published by . This book was released on 1989 with total page pages. Available in PDF, EPUB and Kindle. Book excerpt: L'ETUDE PAR XPS DE LA SURFACE D'ALLIAGES NI CR FE DOPES EN SOUFRE APRES DISSOLUTION ANODIQUE PUIS PASSIVATION A MIS EN EVIDENCE L'INCORPORATION DE SULFURES DE NICKEL DANS LA COUCHE PASSIVE MAJORITAIREMENT CONSTITUEE D'OXYDES DE CHROME. CECI RESULTE D'UNE COMPETITION ENTRE LA CROISSANCE D'OXYDES DE CHROME ET DE SULFURES DE NICKEL SUR LA SURFACE AVANT PASSIVATION

Download or read book ETUDE PAR SPECTROSCOPIE XPS ET ELECTROCHIMIE DE LA PASSIVATION ET DE LA CORROSION LOCALISEE D UN ALLIAGE FE 17 CR EN PRESENCE DE CHLORURES ET DE THIOSULFATES written by WENPING.. YANG YANG and published by . This book was released on 1993 with total page 184 pages. Available in PDF, EPUB and Kindle. Book excerpt: L'OBJET DE CETTE ETUDE EST D'ETUDIER LES FILMS PASSIFS FORMES SUR UN ALLIAGE FE-17%CR EN MILIEU NEUTRE ET EN MILIEU ACIDE, EN PRESENCE D'IONS CHLORURES, EN RELATION AVEC LA RESISTANCE A LA PIQURATION. LA PREMIERE PARTIE DE CE TRAVAIL EST CONSACREE A L'ETUDE DU VIEILLISSEMENT DU FILM PASSIF EN MILIEU NEUTRE (0,02 MNACL). LA MEILLEURE RESISTANCE A LA PIQURATION PAR LE VIEILLISSEMENT DU FILM PASSIF EST DUE A L'ENRICHISSEMENT EN OXYDE DE CHROME DANS LA PARTIE INTERNE DU FILM. LA DEUXIEME PARTIE DE CE TRAVAIL CONCERNE L'ETUDE DU FILM PASSIF EN MILIEU ACIDE SULFURIQUE (0,5 MH#2SO#4) EN ABSENCE OU EN PRESENCE D'IONS CHLORURES. NOUS AVONS MONTRE QUE LA PRESENCE DES IONS CHLORURES EN SOLUTION N'A PAS D'INFLUENCE SUR LA COMPOSITION ET L'EPAISSEUR DU FILM PASSIF ET QUE LES IONS CHLORURES SONT PRESENTS MAJORITAIREMENT DANS LA PARTIE EXTERNE DU FILM, QUEL QUE SOIT LE MOMENT CHOISI POUR INTRODUIRE LES IONS CHLORURES DANS LA SOLUTION (AVANT OU APRES LA FORMATION DU FILM PASSIF). LA DERNIERE PARTIE DE CE TRAVAIL CONSISTE EN L'ETUDE DES EFFETS DES THIOSULFATES EN MILIEU CHLORURE (0,02MNACL) SUR LA PASSIVATION ET LA PIQURATION DE L'ALLIAGE. NOUS AVONS OBSERVE QUE L'INFLUENCE NEFASTE DES IONS S#2O#3#2#- APPARAIT AUSSI BIEN DANS LA MESURE DU POTENTIEL DE PIQURATION QUE DANS L'INHIBITION DU CARACTERE BENEFIQUE DU VIEILLISSEMENT DU FILM PASSIF. CET EFFET NEFASTE EST LIE A LA DECOMPOSITION PAR REDUCTION DES IONS S#2O#3#2#- EN SOUFRE ADSORBE ET/OU EN SULFURE SUR LA SURFACE METALLIQUE DE L'ALLIAGE, INHIBANT AINSI LA REPASSIVATION

Download or read book ETUDE PAR SPECTROSCOPIE XPS ET ELECTROCHIMIE DE LA PASSIVATION ET DE LA CORROSION LOCALISEE D ACIERS INOXYDABLES AUSTENITIQUES TRAITES PAR IMPLANTATION IONIQUE DE MOLYBDENE written by ERIC.. DE VITO and published by . This book was released on 1992 with total page 150 pages. Available in PDF, EPUB and Kindle. Book excerpt: DES ALLIAGES FE-19CR-10NI(AT%) ONT ETE TRAITES PAR IMPLANTATION IONIQUE DE MOLYBDENE (MO#+,100KEV,2.510#1#6AT.CM#-#2). LE PROFIL DE CONCENTRATION DU MOLYBDENE IMPLANTE ETABLI PAR SPECTROSCOPIES XPS ET RBS A MONTRE QUE LA CONCENTRATION DE MO QUI EST DE 4AT% EN SURFACE, PASSE PAR UN MAXIMUM DE 8.5AT% A UNE PROFONDEUR DE 150N ET DECROIT ENSUITE JUSQU'A UNE PROFONDEUR DE 600N. LES EFFETS DU MOLYBDENE IMPLANTE SUR LA PASSIVATION DE L'ALLIAGE EN MILIEU H#2SO#40.5 M ONT ETE ETUDIES EN COUPLANT DES TECHNIQUES ELECTROCHIMIQUES (POTENTIOSTATIQUES, POTENTIOCINETIQUES ET ETDA) A LA SPECTROSCOPIE DE PHOTOELECTRONS (XPS), LES TRANSFERTS D'ECHANTILLONS ETANT EFFECTUES A L'ABRI DE L'AIR. LE COMPORTEMENT ELECTROCHIMIQUE DE L'ALLIAGE EN MILIEU H#2SO#40.5M EST CONSIDERABLEMENT MODIFIE PAR LA PRESENCE DE MO IMPLANTE. LA DISSOLUTION A L'ETAT ACTIF EST INHIBEE ALORS QU'UNE VAGUE D'OXYDATION APPARAIT DANS UNE REGION PLUS ANODIQUE EN POTENTIEL. CETTE VAGUE A ETE EXPLIQUEE PAR UNE DISSOLUTION PREFERENTIELLE DE FER AINSI QUE D'UNE PARTIE DU MOLYBDENE IMPLANTE QUI SE TROUVE ENRICHI A L'ETAT D'OXYDATION +4 DANS LE FILM A L'ETAT ACTIF. CECI EXPLIQUE D'UNE PART L'ENRICHISSEMENT EN ELEMENTS ALLIES SOUS LE FILM PASSIF, D'AUTRE PART LA COMPOSITION ULTERIEURE DU FILM PASSIF. CELUI-CI POSSEDE UNE STRUCTURE BICOUCHE AVEC UNE COUCHE EXTERNE D'HYDROXYDE DE CR RECOUVRANT UNE COUCHE INTERNE D'OXYDES DE FE ET CR. LE MOLYBDENE EST LOCALISE DANS LA PARTIE EXTERNE DU FILM PASSIF MAJORITAIREMENT A L'ETAT D'OXYDATION +6. SON ROLE SERAIT DE FAIRE CROITRE L'EPAISSEUR DU FILM D'HYDROXYDE. LA RESISTANCE A LA DISSOLUTION DANS LE DOMAINE PASSIF N'EST PAS AMELIOREE PAR MO. EN REVANCHE LE ROLE PROTECTEUR DU MOLYBDENE VIS-A-VIS DE LA PIQURATION A ETE CLAIREMENT MIS EN EVIDENCE EN MILIEU CHLORURE. LE MOLYBDENE PIEGERAIT LES IONS CL# LORS DE SA DISSOLUTION AU COURS DE LA FORMATION DU FILM ET PERMETTRAIT AINSI LA PASSIVATION DE L'ALLIAGE

Download or read book ETUDE ANALYTIQUE ET ELECTROCHIMIQUE DES FILMS DE PASSIVATION FORMES EN MILIEU BORATE A LA SURFACE D ALLIAGES INOXYDABLES A BASE DE FER OU DE NICKEL INFLUENCE DE LA TENEUR EN CHROME written by STEPHANE.. BOUDIN and published by . This book was released on 1994 with total page 133 pages. Available in PDF, EPUB and Kindle. Book excerpt: CE MEMOIRE DE THESE EST CONSACRE A L'ETUDE DE LA COMPOSITION DES FILMS DE PASSIVATION FORMES EN MILIEU BORATE (PH=9.2) A LA SURFACE D'ALLIAGES FE-CR ET NI-CR(-FE), DONT LA TENEUR EN CHROME VARIE DE 0 A 30%. APRES UN RAPPEL SUR LES METHODES DE CARACTERISATION ELECTROCHIMIQUE ET LES TECHNIQUES D'ANALYSE DE SURFACE (SPECTROMETRIE AUGER, PHOTOEMISSION X), APPLIQUEES A L'ANALYSE EN PROFONDEUR DES FILMS MINCES DE PASSIVATION, UNE APPROCHE QUANTITATIVE DE LA PROFILOMETRIE AUGER EST PRESENTEE ; CE MODELE, BASE SUR LA NOTION D'ABRASION SEQUENTIELLE, EST EXAMINE DE FACON CRITIQUE POUR LE CALCUL DES PROFILS DE CONCENTRATION. D'APRES LES RESULTATS OBTENUS, NOUS POUVONS DEFINIR POUR CES FILMS UNE STRUCTURE DE TYPE DUPLEX: UNE COUCHE INTERNE ENRICHIE EN CHROME OXYDE, RECOUVERTE, SELON LES ALLIAGES, D'UNE COUCHE D'OXY(HYDROXY)DES DE FER OU DE NICKEL. L'ALLIAGE METALLIQUE SOUS-JACENT EST ALORS SYSTEMATIQUEMENT DEFICITAIRE EN CHROME ; CE GRADIENT SERAIT LA CONSEQUENCE DE LA SEGREGATION DE CET ELEMENT INDUITE PAR L'OXYGENE DURANT L'ETAPE INITIALE DE FORMATION DU FILM. LES PROFILS DE CONCENTRATION ET LES CINETIQUES DE REDUCTION CATHODIQUE CONFIRMENT L'EXISTENCE D'UNE TENEUR CRITIQUE EN CHROME DANS LES DEUX TYPES D'ALLIAGES, SITUEE ENTRE 10 ET 15%, AU-DELA DE LAQUELLE L'OXYDE DE CHROME, PRATIQUEMENT PUR SUR QUELQUES COUCHES ATOMIQUES AU CONTACT DE L'ALLIAGE METALLIQUE, DEVIENT GLOBALEMENT MAJORITAIRE. C'EST EGALEMENT UNIQUEMENT AU-DELA DE CETTE TENEUR QUE L'OXYDE DE CHROME CONSTITUE UNE BARRIERE CONTRE LA DIFFUSION DU FER OU DU NICKEL, QUI CONTROLE LA SECONDE ETAPE DE LA CROISSANCE DU FILM. UN TEL MECANISME A DEUX ETAPES PARAIT JUSTIFIE PAR LES DIFFERENCES D'AFFINITE DES ELEMENTS D'ALLIAGE POUR L'OXYGENE, DE LEUR DIFFUSIVITE DANS LA COUCHE D'OXYDE DE CHROME ET DE LEUR SOLUBILITE EN SOLUTION BORATE