Download or read book ETUDE DE LA PRECIPITATION DE LA PHASE INTERMETALLIQUE NIAL ET DU DURCISSEMENT STRUCTURAL ASSOCIE DANS DES ALLIAGES INOXYDABLES FERRITIQUES A 19 DE CHROME written by ROLAND.. TAILLARD and published by . This book was released on 1979 with total page 170 pages. Available in PDF, EPUB and Kindle. Book excerpt: CHOIX DE LA COMPOSITION, DU MODE D'ELABORATION ET DES TRAITEMENTS THERMIQUES ET THERMOMECANIQUES DES ALLIAGES ETUDIES. ETUDE DES PROPRIETES MICROSTRUCTURALES DES ETATS DURCIS INDISPENSABLES A L'APPROCHE QUANTITATIVE DU DURCISSEMENT DE PRECIPITATION. ETUDE DES MECANISMES DE PRECIPITATION ET DE GROSSISSEMENT DES PARTICULES. PROPRIETES MECANIQUES ET MECANISMES DE DEFORMATION ET DE RUPTURE DES ETATS DURCIS. APPROCHE THEORIQUE DES PROPRIETES MECANIQUES DE CES ETATS VIEILLIS

Download or read book tude de la pr cipitation de la phase interm tallique NiAl et du durcissement structural associ dans des alliages inoxydables ferritiques 19 de chrome written by Roland Taillard (auteur d'une thèse de sciences.) and published by . This book was released on 1979 with total page 56 pages. Available in PDF, EPUB and Kindle. Book excerpt:

Download or read book tude de la pr cipitation de la phase interm tallique Ni A 1 et du durcissement structural associ dans des alliages inoxydables ferritiques 19 de chrome written by Roland Taillard and published by . This book was released on 1979 with total page 165 pages. Available in PDF, EPUB and Kindle. Book excerpt:

Download or read book tude de la pr cipitation de la phase interm tallique NiA1 et du durcissement structural associ dans des alliages inoxydables ferritiques 19 de chrome written by Roland Taillard and published by . This book was released on 1979 with total page pages. Available in PDF, EPUB and Kindle. Book excerpt:

Download or read book Influence des l ments d addition sur la ductilit et les transformations structurales d aciers inoxydables ferritiques a haute teneur en chrome written by Sophie Daboval and published by . This book was released on 1988 with total page 116 pages. Available in PDF, EPUB and Kindle. Book excerpt: Analyse des courbes d'évolution de la résilience en fonction de la température. mise en évidence de deux types de durcissement associés respectivement aux atomes substitutionnels et aux atomes interstitiels. Étude des cinétiques de précipitation des phases intermétalliques formées lors de maintiens entre 700 et 900° C. Description de ces cinétiques par les diagrammes temps - température - début de précipitation. L'évolution des caractéristiques mécaniques au cours des traitements thermiques est essentiellement régie par la précipitation des phases intermétalliques et des phases de laves. Optimisation de la composition chimique de l'acier

Download or read book Durcissement par precipitation des alliages d aluminium written by and published by Ed. Techniques Ingénieur. This book was released on with total page 37 pages. Available in PDF, EPUB and Kindle. Book excerpt:

Download or read book ETUDE DES EVOLUTIONS STRUCTURALES ET DU COMPORTEMENT MECANIQUE ASSOCIE D ALLIAGES INOXYDABLES MARTENSITIQUES A DURCISSEMENT STRUCTURAL DU TYPE EZ3CNDA 13 08 written by Jacques Bonnin and published by . This book was released on 1990 with total page pages. Available in PDF, EPUB and Kindle. Book excerpt: L'ETUDE PORTE SUR LES EVOLUTIONS STRUCTURALES ET LE COMPORTEMENT MECANIQUE ASSOCIE, D'ALLIAGES MARTENSITIQUES A DURCISSEMENT STRUCTURAL DE COMPOSITION: FE-12,5 CR-8,4 NI-2,15 MO-0,95 A 1,21% MASS AL. AU CHAUFFAGE, LA TRANSFORMATION AUSTENITIQUE S'OPERE EN UNE OU DEUX ETAPES SUIVANT LA VITESSE MISE EN UVRE; LES TEMPERATURES DES POINTS DE TRANSFORMATION AUGMENTENT LORSQUE VC CROIT. LE POINT MS VARIE EN FONCTION DE LA TEMPERATURE MAXIMALE ATTEINTE LORS DU TRAITEMENT PREALABLE EN PHASE Y. L'EVOLUTION DE LA DURETE APRES REVENUS ISOCHRONES (4 HEURES) EST CARACTERISEE PAR UN PIC DE DURCISSEMENT, DU A LA PRECIPITATION NIAL, AYANT UN EXTREMUM POUR R=475#OC; POUR DES REVENUS ISOTHERMES EFFECTUES A R=400 ET 450#OC, ON OBSERVE TROIS STADES DE DURCISSEMENT IMPLIQUANT LA FORMATION D'AMAS PUIS DE PRECIPITES DIFFERENTS. POUR R=550 ET 650#OC INTERVIENNENT LES PHENOMENES DE SURVIEILLISSEMENT ET DE FORMATION D'AUSTENITE DE REVERSION. L'INFLUENCE DE L'ALUMINIUM SUR LE DURCISSEMENT EST PREPONDERANT, RM ET R0.002 AUGMENTENT LORSQUE SA TENEUR CROIT. LE GAIN MAXIMAL DE RESISTANCE LIE A LA PRECIPITATION EST: R0.002=700 MPA. LA DECROISSANCE DE RM ET R0.002 POUR 500R625#OC EST LIEE A LA REVERSION. APRES REVENU, POUR UNE MEME QUANTITE D'AUSTENITE DEUX VALEURS R0,002 SONT OBTENUES, LA PLUS FAIBLE ETANT OBSERVEE LORSQU'INTERVIENT LA REMISE EN SOLUTION DES PRECIPITES NIAL. LES TEMPERATURES CARACTERISANT LA TRANSITION DUCTILE/FRAGILE, AINSI QUE LES VALEURS D'ENERGIE DE RUPTURE DU PALIER DUCTILE DE LA COURBE KV=F ( ESSAI) SONT FORTEMENT INFLUENCEES PAR RM. LES DIMENSIONS DE FACETTES DE QUASI-CLIVAGE, OBSERVEES SUR LES SURFACES DE RUPTURE D'EPROUVETTES DE RESILIENCE, CORRESPONDENT AUX TAILLES DES BLOCS DE LATTES DE MARTENSITE, LESQUELS CONSTITUENT DONC LES UNITES STRUCTURALES CONDITIONNANT LES VALEURS DE L'ENERGIE DE RUPTURE. L'ESTIMATION DE LA CONTRAINTE D'ECOULEMENT, A L'AIDE DE LOIS THEORIQUES RECENTES (TENANT COMPTE

Download or read book Etude de l influence de l addition de fer sur le durcissement et la structure de l alliage aluminium cuivre 4 de cuivre written by Daniel Bouvignies and published by . This book was released on 1968 with total page 73 pages. Available in PDF, EPUB and Kindle. Book excerpt: On étudie dans ce mémoire une série d'alliages ternaires Al-Cu-Fe élaborés à partir de métaux purs. La concentration en cuivre est de 4% et constante, celle du fer varie de 0 à 2%. Par examens micrographiques et aux rayons X on montre qu'après homogénéisation à 540C et trempe les alliages contenant jusqu'à 1% de fer comprennent deux phases : une solution solide riche en aluminium dont la sursaturation en cuivre diminue quand la teneur en fer s'élève et une phase intermétallique ternaire Al7Cu2Fe. L'alliage à 2% de fer contient en plus le composé Al3Fe et n'atteint pas l'état d'équilibre défini par le diagramme des phases. L'étude de la précipitation à l'aide des rayons X montre que l'on retrouve dans ces alliages la même séquence de précipitation que dans les alliages binaires Al-Cu, c'est-à-dire : zones G.P ... Thêta''... Thêta' ... Thêta. Le durcissement des alliages Al-Cu-Fe dépend essentiellement de la teneur en cuivre de leur solution solide, les cinétiques étant en général similaires à celles des alliages binaires Al-Cu correspondants. Cependant la présence des précipités insolubles riches en fer introduit certaines différences dans le comportement des alliages ternaires par rapport aux binaires : 1- Au cours du vieillisement à température ambiante et du revenu à 100C on a constaté pour l'alliance à 0,6% de fer que la formation des zones G.P pouvait être empêchée dans certains cas qui semblent dépendre de la répartition du précipité ternaire. 2- Au cours du revenu à 200C l'apparition de thêta est avancée par rapport au binaire. On explique ces différences en supposant que la présence des précipités intermétalliques entraîne au cours de la trempe l'apparition de défauts (dislocations) qui peuvent jouer le rôle de puits de lacunes ou de sites préférentiels pour la nucléation des précipités thêta.