Download or read book ABSORPTION ET DESORPTION DE L HYDROGENE DANS LES ACIERS LIEES AUX OPERATIONS D ELECTROZINGAGE written by LUC.. DEMEULIER and published by . This book was released on 1997 with total page 135 pages. Available in PDF, EPUB and Kindle. Book excerpt: SI UNE ETUDE PRESENTE UN CARACTERE EXPERIMENTAL IMPORTANT, ELLE SE HEURTE RAPIDEMENT A LA REALISATION D'UN TRES GRAND NOMBRE D'ESSAIS, ET PAR CONSEQUENT A DES INTERPRETATIONS COMPLEXES ET FASTIDIEUSES. POUR LEVER CES DIFFICULTES, UNE UTILISATION RATIONNELLE DE LA METHODOLOGIE DES PLANS D'EXPERIENCES PEUT ETRE EFFECTUEE. CET OUTIL A AINSI PERMIS D'ISOLER LES PARAMETRES LES PLUS IMPORTANTS VIS-A-VIS DE L'ABSORPTION ET LA DESORPTION DE L'HYDROGENE AU COURS DU PROCEDE D'ELECTROZINGAGE. NOUS AVONS MONTRE QUE LE PRODUIT PEUT SE DECOMPOSER EN DEUX SOUS-ENSEMBLES AU COMPORTEMENT DIFFERENT : LE SUBSTRAT D'ACIER ET LE DEPOT DE ZINC. LA MEILLEURE METHODE POUR DOSER L'HYDROGENE PIEGE DANS LE DEPOT EST DE REALISER SA FUSION SOUS GAZ VECTEUR ET CETTE QUANTITE EST MODIFIEE PAR LES PARAMETRES SIGNIFICATIFS (C'EST-A-DIRE AYANT UNE INFLUENCE) DU ZINGAGE (CHIMIE DU BAIN, DENSITE DE COURANT, PRESENCE D'ADDITIFS ORGANIQUES ET INTERACTION ENTRE CES DEUX DERNIERS PARAMETRES). CEPENDANT, IL N'EXISTE PAS DE CORRELATION ENTRE CETTE MESURE ET LE RISQUE DE FRAGILISATION PAR L'HYDROGENE. PAR CONTRE, UNE CORRELATION EST OBSERVEE SI NOUS EFFECTUONS LES DOSAGES PAR DESORPTION SOUS VIDE A 300C. NOUS AVONS PU FIXER DES PLAGES DE VALEURS, POUR NOS ACIERS, DE CONCENTRATION CRITIQUE EN HYDROGENE. AINSI, DANS LE CAS DE L'ACIER AU CARBONE XC55 MARTENSITIQUE, UNE VALEUR PRECISE DE LA CONCENTRATION CRITIQUE, 0,75 CM3/100 G DE METAL, A ETE DETERMINEE. CEPENDANT, IL N'EST PAS POSSIBLE DE GENERALISER CETTE LIMITE A TOUS LES ACIERS : EN EFFET, SI LA QUANTITE D'HYDROGENE DIFFUSIBLE NE VARIE PAS AVEC LA COMPOSITION CHIMIQUE OU LE TRAITEMENT THERMIQUE DE L'ACIER, LA CONCENTRATION CRITIQUE, ELLE, EN DEPEND FORTEMENT ; AINSI, ELLE EST INFERIEURE A 0,13 CM3/100 G POUR UN ACIER 42 CD 4 TRAITE A 44/46 HRC, ALORS QUE POUR CE MEME ACIER TRAITE A 37/39 HRC, ELLE EST SUPERIEURE A 0,29 CM3/100 G. LA CONCENTRATION EN HYDROGENE DIFFUSIBLE DANS L'ACIER EST ESSENTIELLEMENT DETERMINEE PAR LA PHASE DE DECAPAGE ACIDE (POUR L'ABSORPTION) ET LE DEGAZAGE INDUSTRIEL (POUR LA DESORPTION). CEPENDANT, L'EFFET LIMITE DE CETTE DERNIERE OPERATION INCITE A IMPOSER UNE MEILLEURE MAITRISE INDUSTRIELLE DU DECAPAGE ACIDE AFIN DE LIMITER L'ABSORPTION DE L'HYDROGENE DANS LE SUBSTRAT. L'OBSERVATION DES FACIES MICROFRACTOGRAPHIQUE DE PIECES CASSEES PAR RUPTURE DIFFEREE A PERMIS DE LEVER, EN PARTIE, L'AMBIGUITE SUR L'ORIGINE DE LA RUPTURE. LORSQUE LE FACIES EST ENTIEREMENT INTERGRANULAIRE ET AVEC UNE GRANDE QUANTITE DE PATTES D'OIE, NOUS POUVONS CONCLURE AVEC CERTITUDE QUE LA RUPTURE EST DUE A L'HYDROGENE EN RELATION AVEC SON PIEGEAGE SUR LES JOINTS DE GRAINS, ET UNE MODIFICATION DES MECANISMES DE DEFORMATION PLASTIQUE.