Download or read book L identification de la calorim trie balayage diff rentiel DSC des conditions de traitement thermique des alliages d aluminium written by Zhixing Chen and published by . This book was released on 2019 with total page pages. Available in PDF, EPUB and Kindle. Book excerpt: Les alliages d'aluminium moulés et forgés sont largement utilisés dans l'industrie automobile et aéronautique. Pour répondre aux différentes exigences pour les différentes applications pratiques, divers processus de traitement thermique sont couramment effectués sur les matériaux, tels que le traitement thermique en solution (SHT), le traitement naturel de vieillissement (T4), le vieillissement artificiel (T5), le vieillissement de pic (T6) et le vieillissement excessif (T7) après SHT. Afin de diagnostiquer rapidement le problème de production des pièces liées au traitement thermique, la méthode de la calorimétrie différentielle à balayage (DSC) est utilisée comme outil dans la présente oeuvre pour identifier les diverses trempes de multiples alliages d'aluminium industriel populaire, à savoir la plaque AlSi10Mg0.3Mn obtenue par le moulage sous vide à haute pression (HPVDC), la barre Al-Si-Cu 319 obtenue par la coulée de moulage permanent (PM), et la feuille extrudée Al-Si-Mg 6082, qui peut être utile en établissant une base de données d'empreintes digitales pour les trempes et les alliages selon la capacité de traçabilité de l'histoire thermique effectuée par DSC. Les résultats obtenus peuvent être divisés en ces deux parties. Dans la première partie, la caractérisation sur les courbes DSC après des trempes différents dans trois alliages, a été effectuée. Les résultats ont montré que divers pics sont apparus sur les courbes DSC, qui ont été caractérisées pour identifier les processus de précipitation ou de dissolution de différentes phases métastables. Le nombre de pics ainsi que la forme des pics varient aussi bien avec les trempes, qui sont résultant de leurs différents comportements de précipitation ou de dissolution. Les trempes F (tel que fabriqué) et SHT peuvent être directement séparées des trempes vieillissantes en raison de la différence sur le nombre de pics, qui sont généralement plus nombreux que ces derniers homologues. Avec les gammes de revenus similaires à la température des pics DSC, la hauteur du pic peut être utilisée pour déterminer les différentes limites zone de pic. Avec des phases métastables ayant des précurseurs plus élevés à l'intérieur de l'alliage sous une certaine trempe, le pic DSC correspondant peut être plus élevé de sorte qu'il soit un point essentiel pour différer les trempes similaires, en particulier parmi les trempes vieillissantes. Pendant ce temps, les microstructures, la conductivité électrique et la micro dureté sous diverses trempes sont également étudiés et leurs résultats peuvent bien soutenir l'évolution des courbes DSC au cours des multiples trempes de différents alliages. Et ces résultats compensent également les limites de la technique de DSC pour identifier les conditions semblables parmi quelques trempes vieillissantes. Pour ce qui est de la deuxième partie, la cinétique de précipitation de l'alliage AlSi10Mg0.3Mn à diverses trempes sont étudiées. Certains pics sur la courbe DSC sont utilisés pour calculer des paramètres cinétiques de précipitation, à savoir l'énergie d'activation. Les résultats montrent que l'énergie d'activation du processus de transformation varie significativement parmi différentes trempes; avec la trempe F étant le plus faible parmi les trempes F et SHT et la trempe T5 étant le plus élevé parmi les trempes vieillissantes. Ces résultats peuvent être utilisés pour expliquer l'évolution de transformation de phase pendant le processus de chauffage DSC. En comparant les résultats d'énergie d'activation, les variations de la cinétique de précipitation de certaines trempes peuvent être affectées par les précipités de précurseur correspondants. Les microstructures sont également étudiées par microscopie électronique en transmission (MET), de sorte que la caractérisation de la cinétique de précipitation à la microstructure soit établie. Par conséquent, différentes conditions traitées thermiquement des alliages industriels étudiés, ont été identifiées pour l'établissement de l'empreinte digitale DSC dans cette présente oeuvre. Cast and wrought aluminum alloys are widely used in automobile and aviation industries. To meet the different requirements for the various practical applications, various heat treatment processes are commonly performed on the materials, such as solution heat treatment (SHT), natural aging treatment (T4), artificial aging (T5), peak aging (T6) and over aging (T7) after SHT. In order to rapidly diagnose the production problem of parts related to heat treatment, the differential scanning calorimetry (DSC) method is used as a tool in present work to identify the various tempers of several popular industrial aluminum alloys, namely AlSi10Mg0.3Mn plate by high pressure vacuum die casting (HPVDC), Al-Si-Cu 319 bar by permanent-mold (PM) casting, and Al-Si-Mg 6082 extruded sheet, which can be useful by establishing a fingerprint database for tempers and alloys according to the thermal history trace ability by DSC. The results obtained can be divided into the following two parts. In the first part, the characterization on DSC curves after different tempers in three alloys has been performed. Results show that various peaks appeared on DSC curves, which have been characterized to identify the precipitation or dissolution processes of different metastable phases. Both the peak number and the peak shape varies with tempers, which are resulted from their different precipitation or dissolution behaviors. F (as-fabricated) and SHT tempers can be directly separated from aging tempers due to the difference on peak number, which are usually more than the latter counterparts. With the similar temperature ranges of the DSC peaks, the peak height can be used to determine the different peak area. With higher precursor metastable phases inside the alloy under the certain temper, the corresponding DSC peak can be higher so that it is an essential point to differ similar tempers, especially among aging tempers. Meanwhile, microstructures, electric conductivity and microhardness under various tempers are also investigated and their results can well support the evolution of DSC curves during the various tempers of different alloys. And those results also compensate the limitations of the DSC technique to identify the similar conditions among some aging tempers. For the second part, precipitation kinetics of AlSi10Mg0.3Mn alloy with various tempers are studied. Certain peaks on DSC curves are used to calculate the precipitation kinetic parameters, i.e., the activation energy. Results show that the activation energy of the transformation process significantly varies among different tempers, with the F temper being the lowest among F and SHT tempers, and T5 temper being the highest among aging tempers. These results can be used to explain the evolution of phase transformation during the DSC heating process. Comparing the activation energy results, the variations of the precipitation kinetics in certain tempers can be affected by the corresponding precursor precipitates. Microstructures are also investigated by transmission electron microscopy (TEM), so that the characterization from precipitation kinetics to microstructure are established. Therefore, different heat-treated conditions of studied industrial alloys have been identified with establishing the DSC fingerprint in the present work.

Download or read book Differential Scanning Calorimetry written by G.W.H. Höhne and published by Springer Science & Business Media. This book was released on 2013-06-29 with total page 233 pages. Available in PDF, EPUB and Kindle. Book excerpt: Differential Scanning Calorimetry (DSC) is a well established measuring method which is used on a large scale in different areas of research, development, and quality inspection and testing. Over a large temperature range, thermal effects can be quickly identified and the relevant temperature and the characteristic caloric values determined using substance quantities in the mg range. Measurement values obtained by DSC allow heat capacity, heat of transition, kinetic data, purity and glass transition to be determined. DSC curves serve to identify substances, to set up phase diagrams and to determine degrees of crystallinity. This book provides, for the first time, an overall description of the most impor tant applications of Differential Scanning Calorimetry. Prerequisites for reliable measurement results, optimum evaluation of the measurement curves and esti mation of the uncertainties of measurement are, however, the knowledge of the theoretical bases of DSC, a precise calibration of the calorimeter and the correct analysis of the measurement curve. The largest part of this book deals with these basic aspects: The theory of DSC is discussed for both heat flux and power compensated instruments; temperature calibration and caloric calibration are described on the basis of thermodynamic principles. Desmearing of the measurement curve in different ways is presented as a method for evaluating the curves of fast transitions.

Download or read book Modulated Temperature Differential Scanning Calorimetry written by Mike Reading and published by Springer Science & Business Media. This book was released on 2006-02-22 with total page 352 pages. Available in PDF, EPUB and Kindle. Book excerpt: MTDSC provides a step-change increase in the power of calorimetry to characterize virtually all polymer systems including curing systems, blends and semicrystalline polymers. It enables hidden transitions to be revealed, miscibility to be accurately assessed, and phases and interfaces in complex blends to be quantified. It also enables crystallinity in complex systems to be measured and provides new insights into melting behaviour. All of this is achieved by a simple modification of conventional DSC. In 1992 a new calorimetric technique was introduced that superimposed a small modulation on top of the conventional linear temperature program typically used in differential scanning calorimetry. This was combined with a method of data analysis that enabled the sample’s response to the linear component of the temperature program to be separated from its response to the periodic component. In this way, for the first time, a signal equivalent to that of conventional DSC was obtained simultaneously with a measure of the sample’s heat capacity from the modulation. The new information this provided sparked a revolution in scanning calorimetry by enabling new insights to be gained into almost all aspects of polymer characteristics. This book provides both a basic and advanced treatment of the theory of the technique followed by a detailed exposition of its application to reacting systems, blends and semicrystalline polymers by the leaders in all of these fields. It is an essential text for anybody interested in calorimetry or polymer characterization, especially if they have found that conventional DSC cannot help them with their problems.

Download or read book Differential Scanning Calorimetry written by Günther Höhne and published by Springer. This book was released on 2014-03-12 with total page 298 pages. Available in PDF, EPUB and Kindle. Book excerpt: In this fully updated and revised second edition the authors provide the newcomer and the experienced practitioner with a balanced and comprehensive insight into all important DSC methods, including a sound presentation of the theoretical basis of DSC and TMDSC measurements. Emphasis is layed on instrumentation, the underlying measurement principles, metrologically correct calibrations, factors influencing the measurement process, and on the exact interpretation of the results. The information given enables the research scientist, the analyst and experienced laboratory staff to apply DSC methods successfully and to measure respective properties correctly.

Download or read book Differential Scanning Calorimetry written by G.W.H. Höhne and published by . This book was released on 2003 with total page 298 pages. Available in PDF, EPUB and Kindle. Book excerpt: In this updated and fully revised second edition, the authors provide the newcomer and the experienced practitioner with a balanced and comprehensive insight into all important methods and aspects of Differential Scanning Calorimetry (DSC), including a sound presentation of the theoretical basis of DSC thermal analysis and temperature-modulated DSC (TMDCS). Emphasis is placed on modern evaluation techniques, instrumentation, the underlying measurement principles, metrologically correct calibrations, factors influencing the measurement process, and on the exact interpretation of the results. The information enables the research scientist, the analyst and experienced laboratory staff to choose the most suitable equipment, to apply DSC methods successfully, to interpret the measurement curve, and thus to measure key properties precisely. In addition, the new edition includes improved instrumental techniques such as Tzerotm and StepScantm, new evaluation techniques, more applications, and the latest references. Calorimetry - Dynamische Differenzkalorimetrie - Thermal Analysis - Thermische Analyse

Download or read book Differential Scanning Calorimetry written by G. W. H. Hohne and published by . This book was released on 2014-01-15 with total page 236 pages. Available in PDF, EPUB and Kindle. Book excerpt:

Download or read book Le traitement thermique des alliages d aluminium written by Aluminum Company of Canada and published by . This book was released on 1944 with total page 32 pages. Available in PDF, EPUB and Kindle. Book excerpt:

Download or read book Calorim trie et analyse thermique sous tous ses aspects written by Journées Méditerranéennes de Calorimétrie et D'Analyse thermique and published by . This book was released on 1993 with total page 555 pages. Available in PDF, EPUB and Kindle. Book excerpt:

Download or read book Analyse calorim trique diff rentielle written by Pierre Claudy and published by Tec & Doc Lavoisier. This book was released on 2005-01-01 with total page 390 pages. Available in PDF, EPUB and Kindle. Book excerpt: Parmi les méthodes thermiques d'analyse, l'analyse calorimétrique différentielle (ACD), plus connue sous le nom de d.s.c. (differential scanning calorimetry), connaît un essor exceptionnel lié à plusieurs avantages : sa commodité de mise en œuvre, la faible masse d'échantillon utilisée et le spectre très large des phénomènes enthalpiques qui peuvent être étudiés. Pierre Claudy propose ici le seul ouvrage de synthèse en langue française consacré à l'ACD. Celle-ci y est présentée en s'appuyant d'une part, sur la thermodynamique et la cinétique, et d'autre part sur la modélisation électrique de la thermique. Les différents types de calorimètres isothermes et d'ACD sont décrits, et leur mode de fonctionnement explicité en utilisant des modèles. En programmation linéaire de la température, les applications proches ou éloignées de l'équilibre thermodynamique sont passées en revue. La programmation non-linéaire (escaliers, rampes plus modulation périodique) est également abordée et illustrée de nombreux cas concrets. Après une étude des méthodes expérimentales et des méthodes et produits d'étalonnage, le vaste champ d'applications de l'ACD est exposé. Les méthodes de mesure de la pureté, de la porosité, de même que les dosages calorimétriques sont décrits par l'auteur dans un grand nombre de cas, tout comme la sécurité des produits chimiques. Conçu dans un cadre théorique utilisant les équations de base accessibles au premier cycle, mais néanmoins tourné vers la pratique industrielle, l'ouvrage soutiendra les professionnels et intéressera un large public depuis les étudiants des IUT, des écoles d'ingénieurs, de l'enseignement universitaire, jusqu'aux industriels en formation continue.