Download or read book Elasticit et endommagement haute temp rature de composites fibreux C SiC written by Marie-Laure Bouchetou and published by . This book was released on 1996 with total page 142 pages. Available in PDF, EPUB and Kindle. Book excerpt: DANS LES COMPOSITES C/SIC, LE DIFFERENTIEL DE DILATATION ENTRE LES FIBRES DE CARBONE ET LA MATRICE DE CARBURE DE SILICIUM ENGENDRE, LORS DU REFROIDISSEMENT POST ELABORATION, LA FORMATION DE MICROFISSURES DANS LA MATRICE. LA PRESENCE DE CES MICROFISSURES CONFERE AU MATERIAU UN COMPORTEMENT MECANIQUE SPECIFIQUE ET CONSTITUE DES VOIES D'ACCES PRIVILEGIEES POUR L'OXYGENE. POUR UNE UTILISATION A HAUTE TEMPERATURE SOUS ATMOSPHERE OXYDANTE, LES COMPOSITES C/SIC DOIVENT DONC ETRE POURVUS D'UNE PROTECTION ANTI-OXYDATION QUI EST, POUR PARTIE, CONSTITUEE D'UNE COUCHE DE SIC (SEAL-COAT) DEPOSEE PAR CVI APRES USINAGE DE LA GEOMETRIE FINALE DE LA PIECE. L'ETUDE DU COMPORTEMENT A HAUTE TEMPERATURE DE CES MATERIAUX A ICI ETE ABORDEE A L'AIDE DE TECHNIQUES ULTRASONORES. LES MESURES DE MODULE D'ELASTICITE AINSI REALISEES ONT, EN PARTICULIER, PERMIS D'ETUDIER LA TENUE A L'OXYDATION D'ECHANTILLONS POURVUS OU NON D'UN SEAL-COAT. EN DEHORS DE TOUT MECANISME D'OXYDATION, L'EVOLUTION DU RESEAU DE MICROFISSURES AVEC LA TEMPERATURE DONNE LIEU A DE FORTES VARIATIONS DU MODULE D'ELASTICITE. SOUS AIR, DEUX STADES D'OXYDATION DES PHASES CARBONEES (FIBRE ET/OU INTERPHASE) ONT ETE MIS EN EVIDENCE SUR DES ECHANTILLONS NON REVETUS. DANS LES PREMIERS INSTANTS, L'OXYDATION D'UNE FAIBLE QUANTITE DE CARBONE DANS LA ZONE MICROPOREUSE DE LA FIBRE ENTRAINE UNE PERTE DE COHESION AU SEIN DU MATERIAU QUI SE TRADUIT PAR UNE FORTE DIMINUTION DU MODULE D'ELASTICITE. PUIS, DANS UN DEUXIEME TEMPS, L'OXYDATION SE PROPAGE VERS LE CUR DES FIBRES ET ENTRAINE UNE PERTE DE MASSE IMPORTANTE. LES CINETIQUES D'OXYDATION ETANT FONCTION DU NOMBRE D'ACCES POUR L'OXYGENE, LA PRESENCE DU SEAL-COAT RALENTIT L'OXYDATION, MAIS LES MECANISMES D'OXYDATION RESTENT IDENTIQUES. L'ETUDE DE L'EFFET DE L'APPLICATION D'UNE CONTRAINTE DE TRACTION SUR L'ENDOMMAGEMENT, A HAUTE TEMPERATURE SOUS ATMOSPHERE NEUTRE, A MIS EN EVIDENCE DES COMPORTEMENTS DIFFERENTS SELON LA TEMPERATURE. CES RESULTATS ONT ETE INTERPRETES SUR LA BASE DES EVOLUTIONS DE LA LIAISON INTERFACIALE